ADCA |
| |
PANTHLENE |
| |
DPT |
| |
OBSH |
| |
ENDOTHERMIC |
| |
MASTERBATCH |
| |
NEOTHLENE |
|
Name of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount of
Gas
Generated
(ml/g) |
Features |
| VINYFOR-AC-3 |
ADCA |
208 |
200 |
Median particle diameter; 19 ;
standard type with high decomposition temperature; decomposes
sharply. |
| VINYFOR-AC-50-S |
ADCA |
208 |
200 |
Median particle diameter; 18 ;
suited for x-linked PE foam by press molding. |
| VINYFOR-AC-3M |
ADCA |
208 |
200 |
Median particle diameter; 8 ;
easily influenced by blowing activator. |
| VINYFOR-AC-R |
ADCA |
208 |
200 |
Median particle diameter; 30 ;
tolerance to thermal hysteresis; little initial decomposition
loss by rolling operation etc. |
| VINYFOR-AC-LQ |
ADCA |
199 |
210 |
Median particle diameter; 20 ;
same as above |
| VINYFOR-AC-1C |
ADCA |
199 |
210 |
Median particle diameter; 7 ;
easily influenced by blowing assistant; very little undecomposed
colour. |
| VINYFOR-AC-1L |
ADCA |
200 |
205～220 |
Crosslinked PE foamed sheet. |
| VINYFOR-AC-K3 |
ADCA |
210 |
200 |
Crosslinked PP foamed sheet; (electron processing
system). |
| VINYFOR-AC-LF |
ADCA |
191 |
180 |
Free flowing type and fine cell for XL polyethylene
foam. |
| VINYFOR-DW-6 |
ADCA |
160 |
198 |
Economical, in that large quantity of gas is generated;
when used for PE high density injection molding, uniform minute
cells free from coloring are generated. |
| VINYFOR-AC-M1-K3 |
ADCA |
201 |
190 |
XL polyethylene foam, fine cell, good dispersion
both for chemical and physical cross-linking. |
| VINYFOR-SW-5 |
ADCA |
205 |
186 |
Suitable for PP high density extrusion molding
because decomposition takes place mainly in the initial period
and process is slow; usable for light-colored extrusion moldings. |
| VINYFOR-AK-2 |
ADCA/DPT |
122 |
111 |
Suitable for pressure foaming of EVA and polybutadiene. |
| EXCELLAR-Q-25 |
ADCA/DPT |
122 |
138 |
Suitable for pressure foaming of PE,EVA; generates
uniform micro cells. |
|
| PAMTHLENE IS A NEWLY DEVELOPEMENT OF HIGH CONCENTRATION OF BLOWING
AGENT AND POLYOLEFINE. |
| SPECIFICATIONS |
CARRIER RESIN:POLYOLEFIN AND OTHERS
BLOWING AGENT:AZODICARBONAMIDE AND OTHERS |
Name of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount of
Gas
Generated
(ml/g) |
Features |
| PANTHLENE H 5340 |
ADCA/LDPE |
200 |
110 |
Suited for XL polyolefine foam by press molding,
bulk density 0.6, specific gravity 1.1. |
Name
of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount
of
Gas
Generated
(ml/g) |
Features |
| CELLUAR-DK-80 |
DPT |
205 |
190 |
Generates bigger quantity of gas. |
| CELLUAR-GX |
DPT |
120 |
118 |
Wet-powdered product made from CELLULAR-D with
blowing agent CELLPASTE; easy to handle. |
| CELLUAR-GX-N |
DPT |
120 |
118 |
Same as above; uniform minute cells are generated. |
| CELLPASTE-K3 |
Urea compound |
116* |
103* |
Decomposition product generated when urea, main
constituent, and blowing agent CELLULAR are used simultaneously;
accelerates vulcanization of rubber. |
| CELLPASTE-K4 |
Urea compound |
128* |
125* |
Same as above. |
| CELLPASTE-K5 |
Urea compound |
134* |
130* |
Same as above; usable for PE, PVC, and other similar
resins when used with blowing agent VINIFOR. |
| CELLPASTE-101 |
Urea compound |
142* |
143* |
Same as above; usable for PE, PVC, and other similar
resins when used with blowing agent VINIFOR. |
|
*Quick decomposition temperature and amount of gas generated
when used simultaneously with D.P.T at 1:1 ratio
|
Name of
Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount
of
Gas
Generated
(ml/g) |
Features |
| NEOCELLBORN-N-5000 |
OBSH |
159 |
125 |
Effective for chloroprene, EPDM, and various resins;
white-type blowing agent requiring no blowing activator. |
| NEOCELLBORN-N-1000S |
OBSH |
159 |
125 |
Superior in dispersion to N-5000; when used for molding
of CR and EPDM, minute cells excellent in touch and appearance
are generated. |
| NEOCELLBORN-N-1000M |
OBSH |
158 |
120 |
Compared with N-5000, rich in fine grains and quick
in decomposition, suitable for PVC wall paper. |
| KS |
OBSH/ADCA |
155 |
170 |
When used for low expansion PVC wall paper, suitable
for whitening and rotary embossing. |
| SPANGCELL-DS-25 |
OBSH/ADCA |
180 |
180 |
Extrusion for PE, PS, RB less yellowish colour. |
| FE-791 |
OBSH/ADCA |
197 |
145 |
Wet-powdered, thus superior in dispersion; easy to
handle. |
Name
of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount
of
Gas
Generated
(ml/g) |
Features |
| FE-512 |
ー |
150 |
150 |
Suitable for extrusion molding of PS and PE. |
| FE-507 |
ー |
130 |
118 |
Suitable for extrusion molding of PS and PE, and
injection styrene-based resins. |
| CELLBORN-SC-K |
ー |
150 |
100 |
PS, PE, PP extrusion. |
| CELLBORN-SC-P |
ー |
150 |
140 |
bigger gas evolution than SC-K. |
|
| BLOWING AGENT MASTERBATCH COMPOUND |
Name
of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount
of
Gas
Generated
(ml/g) |
Features |
| POLYTHLENE-EE-206 |
LDPE |
200 |
175 |
Suitable for injection and extrusion molding of PE,
PP and nylon; high forming pressure. |
| POLYTHLENE-EE-105 |
LDPE |
160 |
95 |
Suitable for injection and extrusion molding of PE
and PP; superior in surfacing and whitening. |
| POLYTHLENE-ES-206(5) |
PS |
210 |
170 |
Suitable for injection molding of PS, modified PEE,
and PPO; high forming pressure |
| POLYTHLENE-ES-207 |
PS |
210 |
105 |
Suitable for injection molding of PS, modified PEE,
PRO; superior in surfacing and whitening. |
| POLYTHLENE-EB-106(5) |
ABS |
210 |
100 |
Suitable for injection molding of ABS and AES; high
forming pressure. |
| POLYTHLENE-EB-207 |
ABS |
210 |
105 |
Suitable for injection molding of ABS superior in surfacing
and whitening. |
|
| NEOTHLENE IS RUBBER MASTERBATCH COMPOUND |
Name
of Product |
Major
Constituent |
Decomposition
Temperature
(℃) |
Amount
of
Gas
Generated
(ml/g) |
Features |
| NEOTHLENE RH 231A |
CSM |
208 |
45 |
ADCA Compound. |
| NEOTHLENE RM 504A |
EPDM |
196 |
75 |
ADCA Compound. |
| NEOTHLENE RC 421 |
SBR |
199 |
85 |
ADCA Compound. |
|
 |